Browsing by Author "Abraham, Eldho"
Now showing 1 - 3 of 3
Results Per Page
Sort Options
- Assessment of the changes in the cellulosic surface of micro and nano banana fibres due to saponin treatmentPublication . Cordeiro, Nereida; Faria, Marisa; Abraham, Eldho; Pothan, Laly A.The effect of saponin on the surface properties of banana fibres was studied by Inverse Gas Chromatography (IGC). Parameters including the dispersive component of the surface energy, surface heterogeneity, surface area, as well as acid-base surface properties were determined for saponin modified banana micro and nanofibres. These parameters show a more extensive saponin coating on the nanofibres with a network formation which is explained by the higher reactivity of nanofibres due to the higher surface energy, specific interaction and higher surface area presented by the nanofibres. The energetic profile indicates that both micro and nanofibres coated with saponin interact with the same, or similar, energy active sites. Saponin treatment reduces considerably the surface area of the fibres, with the consequent decrease in the monolayer capacity. The interaction with the polar probes clearly indicates that saponin treatment creates new polar active sites for specific interactions in both samples. However, the treatment increases predominately the basicity of the fibre surface with more relevance to the nanofibres. This behaviour will lead to better polymer/fibre interaction during composite preparation.
- Biodegradable nanocomposite films based on sodium alginate and cellulose nanofibrilsPublication . Deepa, B.; Abraham, Eldho; Pothan, Laly; Cordeiro, Nereida; Faria, Marisa; Thomas, SabuBiodegradable nanocomposite films were prepared by incorporation of cellulose nanofibrils (CNF) into alginate biopolymer using the solution casting method. The effects of CNF content (2.5, 5, 7.5, 10 and 15 wt %) on mechanical, biodegradability and swelling behavior of the nanocomposite films were determined. The results showed that the tensile modulus value of the nanocomposite films increased from 308 to 1403 MPa with increasing CNF content from 0% to 10%; however, it decreased with further increase of the filler content. Incorporation of CNF also significantly reduced the swelling percentage and water solubility of alginate-based films, with the lower values found for 10 wt % in CNF. Biodegradation studies of the films in soil confirmed that the biodegradation time of alginate/CNF films greatly depends on the CNF content. The results evidence that the stronger intermolecular interaction and molecular compatibility between alginate and CNF components was at 10 wt % in CNF alginate films.
- Utilization of various lignocellulosic biomass for the production of nanocellulose: a comparative studyPublication . Deepa, B.; Abraham, Eldho; Cordeiro, Nereida; Mozetic, Miran; Mathew, Aji P.; Oksman, Kristiina; Faria, Marisa; Thomas, Sabu; Pothan, Laly A.Nanocellulose was successfully extracted from five different lignocellulosic biomass sources viz. banana rachis, sisal, kapok, pineapple leaf and coir using a combination of chemical treatments such as alkaline treatment, bleaching and acid hydrolysis. The shape, size and surface properties of the nanocellulose generally depend on the source and hydrolysis conditions. A comparative study of the fundamental properties of raw material, bleached and nanocellulose was carried out by means of Fourier transform infrared spectroscopy, scanning electron microscopy, atomic force microscopy, transmission electron microscopy, birefringence, X-ray diffraction, inverse gas chromatography and thermogravimetric analysis. Through the characterization of the nanocellulose obtained from different sources, the isolated nanocellulose showed an average diameter in the range of 10–25 nm, high crystallinity, high thermal stability and a great potential to be used with acid coupling agents due to a predominantly basic surface. This work provides an insight into the effective utilization of a variety of plant biomass as a potential source for nanocellulose extraction.